An In-Depth Look at Extrusion - Part 1

This is the first in a series of articles that will cover extrusion from beginning to end, dividing them into logical sections.  It will begin with a general discussion of the history and purpose of extrusion, followed by in-depth look at the equipment, the design and function of each component from the extruder motor to the die, processing techniques, troubleshooting, and more.  Readers are encouraged to ask questions which may be addressed in future articles.

BACKGROUND

Extrusion is simply defined as the forcing of a liquid through a die.  In modern industrial terms, extrusion is the pumping of a liquid through a die to yield the final shape desired.  The liquid forced through the die can be a polymer or a metal, such as molten aluminum.  This series of articles will focus on extrusion of polymers through flat or round dies.

Extrusion, as we know, is today is more than 100 years old.  Early extruders were used to extrude rubber, an elastic material.  As material development progressed, synthetic viscoelastic materials were developed for extrusion.  These materials behaved differently, and the extruder was modified to accommodate these new materials.  Original rubber screws utilized constant depth/variable pitch to compress the rubber material, versus screws for polymers, used variable depth/constant pitch to provide the compression necessary to generate pressure.

The machine used for extrusion is not surprising called an extruder.  Extruders are complex machines which consist of the following components:

  • A motor
  • A drive system to control the motor
  • A gearbox
  • An extruder barrel
  • An extruder screw
  • A system for heating and cooling various extruder components
  • A feed system to introduce plastic pellets into the extruder barrel
  • A filtration system, including break plate and screen changer
  • A die
  • Instrumentation such a temperature, pressure, and thickness measurement
  • Various ancillary equipment such as coextrusion, ozonizing, corona treating

This series of articles will focus on traditional single stage, single screw extrusion without the use of a gear pump.  If questions arise on twin screw extrusion, extruder venting, etc., these issues will be addressed.

PROCESS OVERVIEW

The configuration of an extrusion line depends on whether there is a substrate or not.  Figure 1 below shows the essential components of a blown film line, including the extruder, die assembly, automatic air ring, and bubble cage.  The rotating tower assembly, thickness gauge, corona treater, and winder are not shown. In the blown film process, the extruder or extruders melt plastic pellets and pump the hot, viscous polymer melt into the die, which forms a circular film.  As the film exits the die, it is called by an air ring and transported upwards to the collapsing tower, and then onto the winder.  Blown film line speeds are typically limited to a few hundred feet per minute (100-200 m/min).

Figure 1.  Alpha Marathon 77-layer nanofilm blown film line (Photo by Tom Bezigian)

Cast film lines differ from blown film lines in that the die is flat instead of round, the web is cooled with a chill roll instead of an air ring, and the web is transported horizontally instead of vertically.  The two processes yield films with vastly different properties due to the cooling methods and resins used.

Figure 2 below shows a complete small cast film/extrusion coating line, with the unwind stand to the left, the extruder in the center, and winder to the right.  Included on this line are all the components normally associated with an extrusion coating line, namely an unwind stand, corona treater, liquid primer, flame treating, coating/casting section, 3-extruder system with coextrusion feedblock, beta-gauge, and winder.  The nip roll on this laboratory line can be substituted with an air knife and vacuum box to convert from an extrusion coating configuration to a cast film configuration. Line speeds on this type of equipment frequently exceed 365 m/min (1200 ft/min) and can be as fast as 760 m/min (2500 ft/min).

Figure 2.  The SAM, NA pilot laboratory in Phoenix, New York  (Photo by Tom Bezigian)

Flat sheet extrusion dies are not limited to thin coatings, but can also produce thick sheet for subsequent thermofoming, for example as shown in Figure 3 below.  The extruder itself as well as process conditions essentially can remain the same, as varying end-product thicknesses are governing by take-off speed at a given extruder output and width.

Figure 3.  Extrusion of a 6.35 mm (0.250”) thick 3-layer coextruded ABS sheet out of a 4 meter (10 foot) wide multi-manifold die into a 3-roll calendar stack.  The line speed in this process is about 1 meter per minute (3 feet/minute) (Photo by Tom Bezigian)

THE EXTRUDER

As mentioned early, the extruder has several components, which is depicted in Figure 4 below.  All these pieces fit together to yield a salable product.  A summary of the process follows.

Figure 4.  Extruder Schematic showing major components, from http://slideplayer.com/slide/6557489/23/images/4/Extruder+Schematic.jpg

The extruder motor turns the gears in the gearbox, which is coupled to the extruder screw.  Once the extruder reaches operating temperatures, the screw turns and brings the plastic pellets supplied by the hopper into the barrel.  The pellets are conveyed forward by the pushing action of the screw flight. The volume of the first flight times the bulk density of the pellets times the RPM gives the output per minute. 

As the pellets move forward they encounter a restriction at compression (or melt) section of the screw.  In this section, the channel depth (H) of the screw flight diminishes, causing pressure to rapidly increase in this area.  The pressure forces the pellet against the barrel wall, where friction between the pellet and the barrel wall increases temperature of the pellet, causing it to melt.  The frictional forces acting on the pellet determine what is called the solids conveying angle, which ultimately determines extruder output.  It is critical that all air between the solid plastic pellets be eliminated before melting begins.  Failing to do so will convey air forward, which will contribute to the formation of gels, a generally undesirable defect in the finished product.

As the plastic moves downstream, the average temperature increases, and more and more pellets become molten.  High shear sections may be added into the screw design to ensure complete melting prior to exiting the extruder barrel.

There is a tremendous energy transfer from the screw to the pellets in the compression zone, and pressure within that zone can easily reach 400 bar (~6,000 psi).  The energy to pump and melt the plastic pellets ultimately comes from the extruder motor which is transmitted through the gearbox and the extruder screw.  Once the plastic leaves the compression section, pressure generation ceases, and pressure consumption begins.  Enough pressure must be generated to convey the viscous molten plastic out of the extruder, through the filtration system, piping, coextrusion adapters and die so that a uniform flow exits the die along its circumference or width, depending on geometry.  It is the job of the screw designer to design a screw that will provide the required output and melt temperature.

I will continue next month on the melting mechanism, extrusion physics, and other aspects of screw design.

Tom Bezigian holds a B.S. in Plastics Engineering from the University of Massachusetts–Lowell. He has been affiliated with the converting industry for more than 30 years and writes a column, Poly Ploys, for PFFC. It focuses on the field of polymers, laminations, and coatings with emphasis on R&D, quality assurance, manufacturing, marketing, operations, finance, and expert witness experience in the blown film, cast film, orienting, extrusion coating, and converting industries. He is the owner of PLC Technologies consultancy with over 30 years experience. Contact him at This email address is being protected from spambots. You need JavaScript enabled to view it..

 


Subscribe to PFFC's EClips Newsletter